B35P115 Electrical steel

The "115" in B35P115 refers to the specific value of the magnetic induction, measured in tesla, that the steel can support under a certain magnetic field strength. In other words, it indicates the magnetic performance of the silicon steel.

Overall, B35P115 is a specific type of grain-oriented silicon steel with high magnetic flux density and a nominal thickness of 0.35 millimeters. It is designed for use in high-performance electrical equipment that requires excellent magnetic properties.

Grain Oriented Silicon Steel

B35P115 steel Mechanical Properties

Grade	Nominal thickness（mm）	tensile strength L（N/mm2）	Yield Strength L（N/mm2）	Elongation L（%）	Hardness HV1	Bending frequency (times)	Stacking factor（%）
B35P115	0.35	350	310	11	195	17	98.0

NOTE:.
a detector according to GB / t228-2002, GB / T 19289-2003
b. above are typical values only for reference does not guarantee
c. L direction refers to the rolling direction

B35P115 steel sheet/plate Electromagnetic induction standard

Grade	Nominal thickness（mm）	Theoretical density（kg/dm3）	Maximum core loss P17/50 (W/kg)	minimum magnetic induction B8 （T）
B35P115	0.35	7.65	1.15	1.88